Light Emitting Diode and Fabrication Method Thereof

ABSTRACT

A light-emitting diode includes: an epitaxial-laminated layer having from bottom up: an n-type ohmic contact layer, a first n-type transition layer, an n-type etching-stop layer, a second n-type transition layer, an n-type confinement layer, an active layer, a p-type confinement layer, a p-type transition layer and a p-type window layer; a p electrode on the upper surface of the p-type window layer; a metal bonding layer over the bottom surface of the n-type ohmic contact layer, wherein, the portion corresponding to the p electrode position extends upwards and passes through the n-type ohmic contact layer and the first n-type transition layer, till the n-type etching-stop layer, thereby forming a current distribution adjustment structure such that the injected current would not flow towards the epitaxial-laminated layer right below the p electrode; and a conductive substrate over the bottom surface of the metal bonding layer.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a continuation of, and claims priority to, PCT/CN2016/097760 filed on Sep. 1, 2016, which claims priority to Chinese Patent Application No. 201510674946.0 filed on Oct. 19, 2015. The disclosures of these applications are hereby incorporated by reference in their entirety.

BACKGROUND

In recent years, light-emitting diode (LED) has been widely applied and plays a more and more important role in various fields such as display systems, lighting systems, and automobile tail lights.

SUMMARY

To improve luminance of an AlGaInP-based LED, various embodiments disclosed herein provide a new epitaxial structure and designs a new chip structure to improve luminance effect.

In an aspect, a light emitting diode epitaxial structure is provided, including: a substrate, an epitaxial-laminated layer on the substrate, comprising from bottom to up: an n-type ohmic contact layer, a first n-type transition layer, an n-type etching-stop layer, a second n-type transition layer, an n-type confinement layer, an active layer, a p-type confinement layer, a p-type transition layer and a p-type window layer.

In some embodiments, the first n-type transition layer is an n-type AlGaInP material layer, with doping concentration of at least 7E17 and preferred value of 1E18, and the doping material can be Si, Te, with thickness of at least 1 μm and preferred value of 3 μm; doping concentration of the n-type etching-stop layer is at least 1E18 and the preferred value is 5E18, and the doping material can be Si, Te with thickness of at least 0.05 μm and preferred value of 0.1 μm; the second n-type transition layer is an n-type AlGaInP material layer, with doping concentration at least of 7E17 and preferred value of 1E18, and the doping material can be Si, Te with thickness at least of 0.03 μm and preferred value of 0.05 μm; doping concentration of the p-type window layer is at least 8E17 and preferred value is 1E18, and the doping material can be Mg, Zn, C with thickness at least of 5 μm and preferred value of 10 μm.

In another aspect, an LED chip structure is provided with the aforementioned epitaxial structure, including: an epitaxial-laminated layer, comprising from bottom to up: an n-type ohmic contact layer, a first n-type transition layer, an n-type etching-stop layer, a second n-type transition layer, an n-type confinement layer, an active layer, a p-type confinement layer, a p-type transition layer and a p-type window layer; a p electrode on the upper surface of the p-type window layer; a metal bonding layer above the bottom surface of the n-type ohmic contact layer, wherein, the portion corresponding to the p electrode position extends upwards and passes through the n-type ohmic contact layer and the first n-type transition layer, till the n-type etching-stop layer, thus forming a current distribution adjustment structure so that the injected current would not flow towards the epitaxial-laminated layer right below the p electrode; a conductive substrate located on the bottom surface of the metal bonding layer.

In some embodiments, material of the n-type etching-stop layer is InGaP, GaP, GaAs, AlInP, AlAs, or AlGaAs.

In some embodiments, relationship between area of the p electrode W1 and area of the current distribution adjustment structure W2 is: 1<W2/W1.

In some embodiments, relationship between area of the p electrode W1 and area of the current distribution adjustment structure W2 is: W2/W1=1.2.

In some embodiments, relationship between the total thickness of the n-type etching-stop layer and the second n-type AlGaInP layer T1 and thickness of the first n-type AlGaInP layer T2 is: 5<T2/T1<30.

In some embodiments, relationship between the total thickness of the n-type etching-stop layer and the second n-type AlGaInP layer T1 and thickness of the first n-type AlGaInP layer T2 is: 6<T2/T1<20.

In some embodiments, relationship between the total thickness of the n-type etching-stop layer and the second n-type AlGaInP layer T1 and thickness of the first n-type AlGaInP layer T2 is: T2/T1=20.

In some embodiments, thickness of the p-type window layer is 5-10 μm.

In some embodiments, conductivity of the p-type window layer is higher than that of the first and second n-type transition layers.

In some embodiments, the aforementioned light emitting diode also comprises a mirror system, located between the n-type ohmic contact layer and the metal bonding layer, which extends towards the current distribution adjustment structure and covers upper surface of the current distribution adjustment structure.

In some embodiments, the mirror system also extends and passes through the n-type ohmic contact layer to form a groove.

In another aspect, a fabrication method of an LED is provided, including the following steps: 1) forming an epitaxial-laminated layer via epitaxial growth, comprising from bottom to up: an n-type ohmic contact layer, a first n-type transition layer, an n-type etching-stop layer, a second n-type transition layer, an n-type confinement layer, an active layer, a p-type confinement layer, a p-type transition layer and a p-type window layer; 2) fabricating a p electrode on the upper surface of the p-type window layer; 3) fabricating a metal bonding layer on the bottom surface of the n-type ohmic contact layer, wherein, the portion right below the p electrode position extends upwards and passes through the n-type ohmic contact layer and the first n-type transition layer, till the n-type etching-stop layer, thus forming a current distribution adjustment structure so that the injected current would not flow towards the epitaxial-laminated layer right below the p electrode; 4) providing a conductive substrate and connecting the conductive substrate with the formed metal bonding layer.

The method can adopt substrate transfer technology for twice. At first, after step 2), bind the p-type window layer to the temporary substrate, and remove the growth substrate; and after 4), remove the temporary substrate.

In some embodiments, step 3) specifically includes: etching to remove the n-type ohmic contact layer and the first n-type transition layer right below the p electrode via yellow photochemical process, and stopping etching at the n-type etching-stop layer to form a groove; fabricating a metal bonding layer that fills in the groove structure on the bottom surface of the n-type ohmic contact layer to form a current distribution adjustment structure.

In some embodiments, step 3) also comprises fabrication of a mirror system, specifically: etching to remove the n-type ohmic contact layer and the first n-type transition layer right below the p electrode via yellow photochemical process, and stopping etch at the n-type etching-stop layer to form a groove; fabricating a mirror system on the bottom surface of the n-type ohmic contact layer, which extends towards the groove and covers the side wall and bottom of the groove; fabricating a metal bonding layer on the bottom surface of the mirror system, which fills the groove structure, and forms a current distribution adjustment structure. In some embodiments, the method also comprises: based on luminance efficiency of the light emitting diode, prefer the ratio between the total thickness T1 of the n-type etching-stop layer and the second n-type transition layer and thickness of the first n-type transition layer T2.

In another aspect, a light-emitting system is provided including a plurality of the LEDs described above. The light-emitting system can be used, for example, in lighting, signage, display, etc.

Other features and advantages of various embodiments of the present disclosure will be described in detail in the following specification, and it is believed that such features and advantages will become more apparent in the specification or through implementations of various embodiments disclosed herein. The purposes and other advantages of the embodiments can be realized and obtained in the structures specifically described in the specifications, claims and drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are included to provide a further understanding of the various embodiments disclosed herein and to constitute a part of this specification, together with the embodiments, are therefore to be considered in all respects as illustrative and not restrictive. In addition, the drawings are merely illustrative, which are not drawn to scale.

FIG. 1 illustrates a side sectional view of an AlGaInP-based light emitting diode.

FIG. 2 illustrates a side sectional view of another AlGaInP-based light emitting diode.

FIG. 3 illustrates a side sectional view of the light emitting diode epitaxial structure according to some embodiments.

FIG. 4 illustrates a side sectional view of the light emitting diode structure with the epitaxial structure as shown in FIG. 3.

FIG. 5 shows a luminance enhancing tendency chart of the light emitting diode according to some embodiments.

FIG. 6 shows a flow chart of the fabrication method of the light emitting diode according to some embodiments.

In the drawings:

110, 210: conductive substrate; 120, 220: metal bonding layer; 130, 230: mirror system; 141, 241: n-type ohmic contact layer; 142: n-type transition layer; 143: n-type confinement layer; 144: active layer; 145: p-type confinement layer; 146: p-type AlGaInP layer; 147: window layer; 148: p-type ohmic contact layer; 151, 215: p electrode; 152, 252: n electrode; 242: first n-type transition layer; 243: n-type etching-stop layer; 244: second n-type transition layer; 245: n-type confinement layer; 246: active layer; 247: p-type confinement layer; 248: p-type AlGaInP layer; 249: window layer; 250: p-type ohmic contact layer; current distribution adjustment structure: 260; W1: width of the p electrode; W2: width of the current distribution adjustment structure; T1: total thickness of the n-type etching-stop layer and the second n-type transition layer; T2: thickness of the first n-type transition layer.

DETAILED DESCRIPTION

Various embodiments of the present disclosure will be described in detail with reference to the accompanying drawings and examples, to help understand and practice the disclosed embodiments, regarding how to solve technical problems using technical approaches for achieving the technical effects. It should be understood that the embodiments and their characteristics described in this disclosure may be combined with each other and such technical proposals are deemed to be within the scope of this disclosure without departing from the spirit of this invention.

FIG. 1 illustrates an existing AlGaInP-based light emitting diode structure, which increases luminance by transferring the light-absorbing GaAs substrate into a Si substrate via bonding. Due to overlapping region between the n-type ohmic contact layer and the p-type ohmic contact layer, the current under electrode is evenly distributed on the entire epitaxial structure. Therefore, the light emitted by the light-emitting layer under the p-electrode is absorbed by the p-electrode, thus leading to lower luminance. A structure as shown in FIG. 2 is provided. A non-overlapping design is made between the n-type ohmic contact layer and the p-type ohmic contact layer, so that current would not distribute below p-electrode, thus improving luminance. However, the luminance enhancing effect is insignificant in consideration of the relationship between epitaxial thickness and concentration. FIG. 3 illustrates an epitaxial structure of light emitting diode according to some embodiments disclosed herein, comprising: a GaAs growth substrate 200, an n-type ohmic contact layer 241, a first n-type transition layer 242, an n-type etching-stop layer 243, a second n-type transition layer 244, an n-type confinement layer 245, an active layer 246, a p-type confinement layer 247, a p-type AlGaInP layer 248 and a p-type window layer 249.

In some embodiments, the growth substrate 200 is GaAs; the n-type ohmic contact layer 241 is GaAs; the first n-type transition layer 242 is n-AlGaInP, with doping concentration at least of 7E17 and preferred value of 1E18, and the doping material can be Si, Te with thickness at least of 1 μm and preferred value of 3 μm; material of the n-type etching-stop layer 243 can be InGaP, GaP, GaAs, AlInP, AlAs or AlGaAs, with doping concentration at least of 1E18 and preferred value of 5E18, and the doping material can be Si, Te with thickness at least of 0.05 μm and preferred value of 0.1 μm; the second n-type transition layer 244 is n-AlGaInP, with doping concentration at least of 7E17 and preferred value of 1E18, and the doping material can be Si, Te with thickness at least of 0.03 μm and preferred value of 0.05 μm; the n-type confinement layer 245 is AlGaInP; the active layer 246 is a multiple-quantum well structure; the p-type confinement layer 247 can be AlGaInP; the p-type AlGaInP layer 248 is 0.5-2 μm, and preferred value is 1 μm; the p-type window layer 249 is p-GaP, with doping concentration at least of 8E17 and preferred value of 1E18, and the doping material can be Mg, Zn, C, with thickness at least of 5 μm and preferred value of 10 μm.

FIG. 4 shows a light emitting diode chip structure with the above epitaxial structure, comprising from bottom to up: an n electrode 252, a conductive substrate 210, a metal bonding layer 220, a mirror system 230, an n-type ohmic contact layer 241, a first n-type transition layer 242, an n-type etching-stop layer 243, a second n-type transition layer 244, an n-type confinement layer 245, an active layer 246, a p-type confinement layer 247, a p-type AlGaInP layer 248, a p-type window layer 249, a p-type ohmic contact layer 250 and a p electrode 251.

Wherein, the portion of the mirror system 230 located right below the p electrode 251 extends upwards and passes through the n-type ohmic contact layer 241 and the first n-type AlGaInP layer 242, till the n-type etching-stop layer 243 to form a groove; the metal bonding layer fills in the groove to form a current distribution adjustment structure 260 so that injected current would not flow to the epitaxial-laminated layer right below the p electrode. With reference to FIG. 4, in this embodiment, width of the current distribution adjustment structure width W2 is larger than the width of p electrode W1, thereby ensuring that no current is flowed to the epitaxial-laminated layer right below the p electrode.

Further, in this embodiment, preferred ratios between the total thickness T1 of the n-type etching-stop layer and the second n-type transition layer and thickness of the first n-type transition layer T2 are selected based on the LED light emission efficiency. FIG. 5 shows the luminance enhancing tendency of the embodiment. Specifically, under fixed W2/W1=1.2, luminance of light emitting diode will increase as ratio T2/T1 increases and tends to be stable when T2/T1>20; therefore, T2/T1 ratio is preferred to be 20.

Detailed descriptions will be given to the fabrication method for the light emitting diode with reference to FIG. 6.

First, form an epitaxial structure as shown in FIG. 3 through epitaxial growth; second, fabricate a p-type ohmic contact layer 250 and a p electrode 251 on the surface of the p-type window layer 249; next, bind the p-type window layer 249 with a temporary substrate (such as glass substrate) via electric resin and remove the growth substrate 200 to expose the n-type ohmic contact layer; next, etch to remove the n-type ohmic contact layer 241 and the first n-type transition layer 242 right below the p electrode via yellow photochemical process; stop etching at the n-type etching-stop layer 243 to form a groove. Specifically, heat 50° C. etching solution with HCL:H2O:H2O2(1:20:1.5) to etch the n-type ohmic contact layer 241 and the first n-type transition layer 242; stop effective etching at the n-type etching-stop layer 243 to form a current distribution adjustment structure through selection ratio of material the n-type etching-stop layer 243 for the etching solution. The structure is wider than the p electrode. Then, fabricate a mirror system and a metal bonding layer; at last, provide a conductive substrate 210, and connect it to the formed metal bonding layer 220, and remove the temporary substrate to form a light emitting diode.

Although specific embodiments have been described above in detail, the description is merely for purposes of illustration. It should be appreciated, therefore, that many aspects described above are not intended as required or essential elements unless explicitly stated otherwise. Various modifications of, and equivalent acts corresponding to, the disclosed aspects of the exemplary embodiments, in addition to those described above, can be made by a person of ordinary skill in the art, having the benefit of the present disclosure, without departing from the spirit and scope of the disclosure defined in the following claims, the scope of which is to be accorded the broadest interpretation so as to encompass such modifications and equivalent structures. 

1. A light-emitting diode, comprising: an epitaxial-laminated layer, comprising from bottom to up: an n-type ohmic contact layer; a first n-type transition layer; an n-type etching-stop layer; a second n-type transition layer; an n-type confinement layer; an active layer; a p-type confinement layer; a p-type transition layer; and a p-type window layer; a p electrode over an upper surface of the p-type window layer; a metal bonding layer over a bottom surface of the n-type ohmic contact layer, wherein: a portion corresponding to a position of the p electrode extends upwards and passes through the n-type ohmic contact layer and the first n-type transition layer, till the n-type etching-stop layer, thereby forming a current distribution adjustment structure such that injected current does not flow towards the epitaxial-laminated layer right below the p electrode; and a conductive substrate located over a bottom surface of the metal bonding layer.
 2. The light-emitting diode of claim 1, wherein: the n-type etching-stop layer is composed of at least one of InGaP, GaP, GaAs, AlInP, AlAs, or AlGaAs.
 3. The light-emitting diode of claim 1, wherein: the first and second n-type transition layers comprise an AlGaInP layer.
 4. The light-emitting diode of claim 1, wherein: relationship between a width of the p electrode W1 and a width of the current distribution adjustment structure W2 is: 1<W2/W1.
 5. The light-emitting diode of claim 1, wherein: relationship between an area of the p electrode W1 and an area of the current distribution adjustment structure W2 is: W2/W1=1.2.
 6. The light-emitting diode of claim 1, wherein: relationship between a total thickness of the n-type etching-stop layer and the second n-type transition layer T1 and a thickness of the first n-type transition layer T2 is: 5<T2/T1<30.
 7. The light-emitting diode of claim 6, wherein: a thickness of the p-type window layer is 5-10 μm.
 8. The light-emitting diode of claim 1, wherein: the n-type etch-stopping layer has a doping concentration higher than 1E18, and a thickness more than 0.05 μm.
 9. The light-emitting diode of claim 1, wherein: the p-type window layer has a doping concentration higher than 8E17, and a thickness more than 5 μm.
 10. The light-emitting diode of claim 1, wherein: a conductivity of the p-type window layer is higher than that of the first and second n-type transition layers.
 11. The light-emitting diode of claim 1, further comprising a mirror system, located between the n-type ohmic contact layer and the metal bonding layer, which extends towards the current distribution adjustment structure and covers upper surface of the current distribution adjustment structure.
 12. The light-emitting diode of claim 11, wherein: the mirror system also extends and passes through the n-type ohmic contact layer to form a groove.
 13. A light-emitting diode fabrication method, comprising: 1) forming an epitaxial-laminated layer, comprising from bottom to up: an n-type ohmic contact layer, a first n-type transition layer, an n-type etching-stop layer, a second n-type transition layer, an n-type confinement layer, an active layer, a p-type confinement layer, a p-type transition layer and a p-type window layer; 2) forming a p electrode on the upper surface of the p-type window layer; 3) forming a metal bonding layer above the bottom surface of the n-type ohmic contact layer, wherein, the portion right below the p electrode position extends upwards and passes through the n-type ohmic contact layer and the first n-type transition layer, till the n-type etching-stop layer, thus forming a current distribution adjustment structure so that the injected current would not flow towards the epitaxial-laminated layer right below the p electrode; and 4) providing a conductive substrate and binding it with the formed metal bonding layer.
 14. The method of claim 13, wherein: step 3) includes: etching to remove the n-type ohmic contact layer and the first n-type transition layer right below the p electrode via yellow photochemical process, and stopping etching at the n-type etching-stop layer to form a groove; fabricating a metal bonding layer that fills in the groove structure on the bottom surface of the n-type ohmic contact layer to form a current distribution adjustment structure.
 15. The method of claim 14, wherein: the step 3) further comprises fabrication of a mirror system, including: etching to remove the n-type ohmic contact layer and the first n-type transition layer right below the p electrode via yellow photochemical process, and stopping etching at the n-type etching-stop layer to form a groove; fabricating a mirror system on the bottom surface of the n-type ohmic contact layer, which extends towards the groove and covers the side wall and bottom of the groove; and fabricating a metal bonding layer on the bottom surface of the mirror system, which fills in the groove structure, and forms a current distribution adjustment structure.
 16. The method of claim 13, wherein: material of the n-type etching-stop layer formed in step 1) is InGaP, GaP, GaAs, AlInP, AlAs, or AlGaAs.
 17. The method of claim 13, wherein: the method also comprises: based on luminance efficiency of the light emitting diode, prefer the ratio between the total thickness T1 of the n-type etching-stop layer and the second n-type transition layer and thickness of the first n-type transition layer T2.
 18. A light-emitting system comprising a plurality of light-emitting diodes (LEDs), each LED including: an epitaxial-laminated layer, comprising from bottom to up: an n-type ohmic contact layer; a first n-type transition layer; an n-type etching-stop layer; a second n-type transition layer; an n-type confinement layer; an active layer; a p-type confinement layer; a p-type transition layer; and a p-type window layer; a p electrode over an upper surface of the p-type window layer; a metal bonding layer over a bottom surface of the n-type ohmic contact layer, wherein: a portion corresponding to a position of the p electrode extends upwards and passes through the n-type ohmic contact layer and the first n-type transition layer, till the n-type etching-stop layer, thereby forming a current distribution adjustment structure such that injected current does not flow towards the epitaxial-laminated layer right below the p electrode; and a conductive substrate located over a bottom surface of the metal bonding layer.
 19. The system of claim 18, wherein: relationship between a width of the p electrode W1 and a width of the current distribution adjustment structure W2 is: 1<W2/W1.
 20. The system of claim 18, wherein: relationship between a total thickness of the n-type etching-stop layer and the second n-type transition layer T1 and a thickness of the first n-type transition layer T2 is: 5<T2/T1<30. 